MIG Welding Wire

The wire is used for electric arc welding of stainless steel using inert gas shield (Metal Inert Gas). Certificates / Approvals: DB, DNV, TÜV.

Welding wire MIG 308L-Si/MVR-Si

                   

Grade	308L–Si/MVR–Si
Standard designations	Acc. to EN 12072					Acc. to AWS A5.9
	19 9 L Si					E308LSi
Package type	on reels
Dimensions, mm (reel weight, kg)	0.8 (12–15) 1.0 (12–15) 1.2 (12–15) 1.6 (12–15)
Welding steel grades	designation EN		designation ASTM						designation GOST
	1.4301 1.4306 1.4307 1.4311 1.4541		304 304L 304L 304LN 321						08H18N10 03H18N11 03H18N11 – 08H18N10T
Chemical composition, %	C	Si	Mn	Cr			Ni		Ferrite*
	0.02	0.85	1.8	20			10.5		11FN
Type	Austenitic
Weld metal mechanical properties	RP0.2, MPa	Rm, MPa	A5,		Impact strength, KV, J				HB
			%		+20°S			–196°S
	420	600	36		110			60	200

Welding wire MIG 310

           

Grade	310
Package type	on reels
Dimensions, mm (reel weight, kg)	0.8 (12–15) 1.0 (12–15) 1.2 (12–15) 1.6 (12–15)
Welding steel grades	designation EN				designation ASTM				designation GOST
	1.4845				310S				10H23N18
Chemical composition, %	C	Si		Mn	Cr	Ni	Mo			Ferrit
	0.02	0.85		1.7	18.5	12	2.6			9 FN
Type	Fully austenitic
Weld metal mechanical properties	RP0.2, MPa		Rm, MPa		A5, %	Impact strength, KV, J				HB
						+20°S		-196°S
	360		570		35	120		–		210

Welding wire MIG 316L-Si/SKR-Si

                   

Grade	316L–Si/SKR–Si
Standard designations	Acc. to EN 12072						Acc. to AWS A5.9
	19 12 3 L Si						E316LSi
Package type	on reels
Dimensions, mm (reel weight, kg)	0.8 (12–15) 1.0 (12–15) 1.2 (12–15) 1.6 (12–15)
Welding steel grades	designation EN				designation ASTM					designation GOST
	1.4436 1.4432 1.4571 1.4401 1.4404 1.4435 1.4406				316 316L 316Ti 316 316L 316L 316LN					06H17N13M2 06H17N14M3 08H17N13M2T 06H17N13M2 04H17N13M2 04H17N13M2 -
Chemical composition, %	C	Si		Mn	Cr	Ni		Mo		Ferrite*
	0.02	0.85		1.7	18.5	12		2.6		9 FN
Type	Austenitic
Weld metal mechanical properties	RP0.2, MPa		Rm, MPa		A5, %	Impact strength, KV, J				HB
						+20°S			-196°S
	400		600		35	110			50	210

Comments:
Wire of the following grades can be supplied

Type acc. to EN 12072	Grade
Martensitic	739 S, 248 SV
Austenitic (ferrite max 10 %)	308L/MVR, 308H, 347–Si/MVNb–Si, , 316L/SKR, 318–Si/SKNb–Si, 317L/SNR
Austenitc-ferritic	2304, 2205, 2507/P100
Fully austenitic	904L, P12, P16, P54
Special types	307–Si, 309L–Si, 309L, 309L–HF, P5, P7, 10
Heat resisting	309–Si, 253 MA, 353 MA

Typical ferrite content, calculated in weld metal using Schaeffler Delong method

• RP0.,2 – yield point, MPa;
• Rm – tensile strength, MPa; ;
• A5 - stretch ratio,%;
• NV – Brinell hardness.